This investigation explores fatigue performance of laser powder bed fusion (LPBF)-fabricated AlSi10Mg alloy subjected to various post-processing treatments: stress relief (SR), Hot Isostatic Pressing (HIP), and HIP + T6, all followed by prolonged thermal aging at 177 °C for up to 1000 h. Microstructural evolution, hardness, density, and uniaxial fatigue performance, including SEM fractography, were examined to recommend practical service life thresholds. Microstructural analysis confirmed that HIP and HIP + T6 treatments effectively eliminated process induced lack of fusion porosity, which was identified as the direct cause of premature elastic regime failure in SR-treated samples. While HIP + T6 achieved the highest initial hardness, both HIP-treated groups showed susceptibility to thermal degradation. The HIP-only samples, in particular, suffered a fatigue life reduction of up to 38% after just 10 h of aging. Fracture analysis showed that unaged SR samples failed in a comparatively more brittle manner, characterized by tear ridges, whereas HIP and HIP + T6 samples displayed an initially ductile fracture with prominent dimple features. Prolonged aging caused the HIP + T6 samples to replace ductile dimple features with a mix of dimple features along with uneven patterns, which may correlate with their decreased fatigue performance. The results of this paper conclusively demonstrate that while HIP post- processing provides robust initial fatigue strength, its benefits are severely compromised by thermal exposure. And for applications limited to the elastic regime, SR post-processing may be suitable, as long as printing parameters are optimized to prevent lack of fusion defects.
- Open Access
- Article
Influence of Heat Treatment and Thermal Aging on the Fatigue Performance of LPBF Fabricated AlSi10Mg Alloy
- Luis A. Marquez 1,2,
- Edel Arrieta 1,3,
- Lawrence E. Murr 1,2,
- Diego A. Ariza 1,
- Mark Benedict 4,
- Jason Thomas 5,
- James Carney 1,
- Francisco Medina 1,3
Author Information
Received: 10 May 2026 | Revised: 23 Jul 2026 | Accepted: 29 Jul 2026 | Published: 28 Aug 2026
Abstract
Keywords
AlSi10Mg alloy | laser powder bed fusion | stress relief | hot isostatic pressing | microstructure | fractography | tensile | hardness and fatigue testing
References
- 1.
Li, S.-S.; Yue, X.; Li, Q.-Y.; et al. Development and Applications of Aluminum Alloys for Aerospace Industry. J. Mater. Res. Technol. 2023, 27, 944–983.
- 2.
Budgen, N.F. The Heat-Treatment and Annealing of Aluminum and Its Alloys; Chapman & Hall: Boca Raton, FL, USA, 1932.
- 3.
Bronco, R.; Berto, F.; Katossos, A. (Eds.) Mechanical Behavior of Aluminum Alloys; MDPI Publishers: Basel, Switzerland, 2018; 144p.
- 4.
Totten, G. (Ed.) Heat Treating Aluminum and Its Alloys; ASM International: Materials Park, OH, USA, 2016.
- 5.
Glazooff, M.; Zoltotorevsky, V.; Blev, N. Casting Aluminum Alloys, 1st ed.; Elsevier Science: New York, NY, USA, 2007.
- 6.
Yan, Q.; Song, B.; Shi, Y. Comparative Study of Performance Comparison of AlSi10Mg Alloy Prepared by Selective Laser Melting and Casting. J. Mater. Sci. Technol. 2020, 41, 1990208.
- 7.
Beder, M.; Akcay, S.B.; Varol, T.; et al. The Effect of Heat Treatment on the Mechanical Properties and Oxidation Resistance of AlSi10Mg Alloy. Arab. J. Sci. Eng. 2024, 49, 15335–15346.
- 8.
Limbasiya, N.; Jain, A.; Soni, H.; et al. A Comprehensive Review on the Effect of Process Parameters and Post-Process Treatments on Microstructure and Mechanical Properties of Selective Laser Melting of AlSi10Mg. J. Mater. Res. Technol. 2022, 21, 1141–1176.
- 9.
Raja, A.; Cheethirala, S.R.; Gupta, P.; et al. A Review on the Fatigue Behavior of AlSi10Mg Alloy Fabricated Using Laser Powder Bed Fusion Technique. J. Mater. Res. Technol. 2022, 17, 1013–1029.
- 10.
Dong, Z.; Xu, M.; Guo, H.; et al. Microstructural Evolution and Characterization of AlSi10Mg Alloy Manufactured by Selective Laser Melting. J. Mater. Res. Technol. 2022, 17, 2343– 2354.
- 11.
Mao, B.; Chu, S.; Chen, S.; et al. On the Mechanical Behavior of Additively Manufactured AlSi10Mg Processed by Post Heat Treatment: The Role of Hierarchically Heterogeneous Microstructure. J. Alloys Compd. 2025, 1038, 182896.
- 12.
Baig, S.; Ghiaasiaan, R.; Shao, S.; et al. Tensile and Fatigue Behaviors of Additively Manufactured AlSi10Mg: Effect of Solutionizing and Aging Heat Treatments. Fatigue Fract. Eng. Mater. Struct. 2023, 46, 2662–2680.
- 13.
Zhang, C.; Zhu, H.; Liao, H.; et al. Effect of Heat Treatment in Fatigue Property of Selective Laser Melting of AlSi10Mg. Int. J. Fatigue 2018, 116, 513–522.
- 14.
Fini, S.; Croccolo, D.; De Agostinis, M.; et al. Fatigue Response of AlSi10Mg by Laser Powder Bed Fusion: Influence of Build Orientation, Heat and Surface Treatments. Prog. Addit. Manuf. 2025, 10, 1385–1403.
- 15.
Roveda, I.; Serrano-Munoz, I.; Haubrich, J.; et al. Investigation of the Fatigue Strength of AlSi10Mg Fabricated by PBF-LD/M and Subjected to Low Temperature Heat Treatments. Mater. Des. 2024, 244, 113170.
- 16.
Ngnekou, J.N.D.; Nadot, Y.; Henaff, G.; et al. Fatigue Properties of AlSi10Mg Produced by Additive Layer Manufacturing. Int. J. Fatigue 2019, 119, 160–172.
- 17.
Ertugrul, O.; Oter, Z.C.; Yilmaz, M.S.; et al. Effect of HIP Process and Subsequent Heat Treatment on Microstructure and Mechanical Properties of Direct Metal Laser Sintered AlSi10Mg Alloy. Rapid Prototyp. J. 2020, 26, 1421–1434.
- 18.
Ramavajjala, A.K.; Dandekar, T.R.; Khatirkar, R.K.; et al. A Review on the Correlation between Microstructure, Heat Treatment and Mechanical Properties of Additively Manufactured AlSi10Mg by LPBF. Crit. Rev. Solid State Mater. Sci. 2025, 50, 239–274.
- 19.
Fernandes, R.F.; Jesus, J.; Borrego, L.; et al. Effect of Heat Treatment on the Fatigue Crack Growth Performance of AlSi10Mg Aluminum Alloy Submitted by LPBF. Procedia Struct. Integr. 2022, 42, 1054–1060.
- 20.
Merino, J.; Ruvalcaba, B.; Varela, J.; et al. Multiple Comparative Heat Treatment and Aging Schedules for Controlling the Microstructures and Mechanical Properties of Laser Powder Bed Fusion Fabricated AlSi10Mg Alloy. J. Mater. Res. Technol. 2021, 13, 669–685.
- 21.
Medrano, V.; Arrieta, E.; Merino, J.; et al. A Comprehensive and Comparative Study of Microstructure and Mechanical Properties for Post-Process Heat Treatment of AlSi7Mg Alloy Components Fabricated in Different Laser Powder Bed Fusion Systems. J. Mater. Res. Technol. 2023, 24, 6820–6842.
- 22.
Zhao, L.; Macías, J.G.S.; Ding, L.; et al. Damage Mechanisms in Selective Laser Melted AlSi10Mg under as Built and Different Post-Treatment Conditions. Mater. Sci. Eng. A 2019, 764, 138210.
- 23.
Syrlybayev, D.; Perveen, A.; Talamona, D. Controlling Mechanical Properties and Energy Absorption in AlSi10Mg Lattice Structures through Solution and Aging Heat Treatments. Mater. Sci. Eng. A 2023, 889, 145843.
- 24.
Růžičková, L.; Sobotová, J.; Beránek, L.; et al. Influence of Stress Relief Annealing Parameters on Mechanical Properties and Decomposition of Eutectic Si Network of L-PBF Additive Manufactured Alloy AlSi10Mg. Metals 2022, 12, 1497.
- 25.
Lehmhus, D.; Rahn, T.; Struss, A.; et al. High-Temperature Mechanical Properties of Stress-Relieved AlSi10Mg Produced via Laser Powder Bed Fusion Additive Manufacturing. Materials 2022, 15, 7386.
- 26.
Zhou, L.; Mehta, A.; Schulz, E.; et al. Microstructure, Precipitates and Hardness of Selectively Laser Melted AlSi10Mg Alloy before and after Heat Treatment. Mater. Charact. 2018, 143, 5–17.
- 27.
Wu, Z.; Wu, S.; Gao, X.; et al. The Role of Internal Defects on Anisotropic Tensile Failure of L-PBF AlSi10Mg Alloys. Sci. Rep. 2023, 13, 14681.
- 28.
Cáceres, C. On the Effect of Macroporosity on the Tensile Properties of the Al-7%Si-0.4%Mg Casting Alloy. Scr. Met. Mater. 1995, 32, 1851–1856.
- 29.
Finfrock, C.B.; Exil, A.; Carroll, J.D.; et al. Effect of Hot Isostatic Pressing and Powder Feedstock on Porosity, Microstructure, and Mechanical Properties of Selective Laser Melted AlSi10Mg. Met. Microstruct. Anal. 2018, 7, 443–456.
- 30.
Sajadi, F.; Tiemann, J.; Bandari, N.; et al. Fatigue Improvement of AlSi10Mg Fabricated by Laser-Based Powder Bed Fusion through Heat Treatment. Metals 2021, 11, 683.
- 31.
Hu, X.; Zhao, G.; Jiang, Y.; et al. Experimental Investigation on the LCF Behavior Affected by Manufacturing Defects and Creep Damage of One Selective Laser Melting Nickel- Based Superalloy at 815 °C. Acta Met. Sin. 2019, 33, 514–527.
- 32.
Tocci, M.; Pola, A.; Gelfi, M.; et al. Effect of a New High-Pressure Heat Treatment on Additively Manufactured AlSi10Mg Alloy. Met. Mater. Trans. A 2020, 51, 4799–4811.
This work is licensed under a Creative Commons Attribution 4.0 International License.
Suite 4002 Level 4, 447 Collins Street, Melbourne, Victoria 3000, Australia
General Inquiries: info@sciltp.com